Aluminium foam tube is a metal that consists of porous medium with special characteristics such as good energy absorption, good heat transfer and high thermal conductivity. These make it suitable to be used in a wide range of applications such as in heat exchangers. The aim of this project is to identify and analyse mechanical behaviour and microstructure aluminium foam tube produced and fabricated with infiltration method with vacuum-gas. The density of aluminium foam tube was also determined and an average aluminium foam tube with porosity 50% - 80% with the average NaCl particle size 2mm, 3mm and 4mm was produced. Foams with porosity 60%-75% NaCl has higher energy absorption. These was based on foam structure, density and maximum compressive load test result.