Microstructural, surface roughness and wettability of titanium alloy coated by YZP-30wt. % TiO2 for dental application
Afida Jemat1, Mariyam Jameelah Ghazali2, Masfueh Razali3, Otsuka, Yuichi4.
Various roughness and surface topography of titanium coated ceramic material have been developed and used in clinical trials especially in a medical implant. The present work aimed to investigate the phase and microstructural of the yttria stabilized zirconia (YZP) coating reinforced titania (TiO2) and its effects on wettability for dental implant application. Plasma spray technique was used to prepare the pure YZP and YZP-30 wt.% TiO2 coatings. The titanium alloys coated with YZP/TiO2 were investigated through scanning electron microscopy (SEM) analysis, roughness measurements, and contact angle analysis. The SEM analysis demonstrated a distinguished lamellae structure of YZP and TiO2 in the coating. Instead of low wettability, the YZP-30 wt.% TiO2 ceramic coating demonstrated high porosity and surface roughness (7.97±0.4 µm) than the pure YZP coating (7.06±0.9 µm) that is beneficial for cell growth and attachment.
Affiliation:
- Universiti Kebangsaan Malaysia, Malaysia
- Universiti Kebangsaan Malaysia, Malaysia
- Universiti Kebangsaan Malaysia, Malaysia
- Nagaoka University of Technology, Japan
Toggle translation
Download this article (This article has been downloaded 150 time(s))
|
|
Indexation |
Indexed by |
MyJurnal (2021) |
H-Index
|
6 |
Immediacy Index
|
0.000 |
Rank |
0 |
Indexed by |
Scopus 2020 |
Impact Factor
|
CiteScore (1.4) |
Rank |
Q3 (Engineering (all)) |
Additional Information |
SJR (0.191) |
|
|
|
|
|