Enhancing the electrical properties of porous silicon photodetector by depositing MWCNTs
Ahmed N.Abd1, Hazim L. Mansour2, Nadir F. Habubi3, Ali H. Reshak4, Ali H. Reshak5.
In the present work, multiwall carbon nanotubes (MWCNTs) layers dispersed in DMF and citric acid deposited by drop casting on porous silicon (PSi) photodetector have been prepared by electrochemical etching (ECE) process at 25 mA/cm2 for 20 min. X-ray diffraction (XRD), atomic force microscopy (AFM), Fourier transformation infrared spectroscopy (FTIR), energy dispersive X-ray (EDX), current–voltage (I-V) characteristics, capacitance-voltage(C-V) characteristics, spectral responsivity (Rλ) and specific detectivity (D*) before and after depositing MWCNTs layers were investigated. It was found that, the On/Off ratio was increased after depositing MWCNTs, while ideality factor and built in potential were decreased and this fact indicates that Al/PSi/c-Si/Al photodetector was nearly approaching the ideal diode characteristic after deposition process. Significant enhancement in spectral responsivity and specific detectivity were also noticed after depositing MWCNTs on porous matrix.
Affiliation:
- University of Mustansiriyah, Iraq
- University of Mustansiriyah, Iraq
- University of Mustansiriyah, Iraq
- University of West Bohemia, Czech Republic
- Universiti Malaysia Perlis, Malaysia
Download this article (This article has been downloaded 79 time(s))
|
|
Indexation |
Indexed by |
MyJurnal (2021) |
H-Index
|
2 |
Immediacy Index
|
0.000 |
Rank |
0 |
Indexed by |
Scopus 2020 |
Impact Factor
|
CiteScore (1.3) |
Rank |
Q3 (Electrical and Electronic Engineering)) Q4 (Electronic, Optical and Magnetic Materials) |
Additional Information |
SJR (0.298) |
|
|
|