Aprilia1, Sri Kunarti2, Theresia Indah Budhy S3, Anggun Prawira Khoirunissak4, Wa Ode Siti Amaliyah Wulandari5, Rima Parwati Sari6, Linda Rochyani7.
Introduction: Anadara-granosa synthesization through hydrothermal-method produces beta-tricalcium(beta-TCP), a biomaterial that is able to provide a pathway for calcium-ions in dentin reparative formation thus qualifies TCP as pulp-capping material.Nanoencapsulation is needed as calcium-ions have shown its rapid solubility which is the main cause of high probability risk of tunnel defect.The present study aimed to understand the correlation between stirring time, particle size and level of calcium of beta-TCP nanoencapsulation synthesized from Anadara-grano- sa-shells. Methods: Anadara-granosa-shells powder was hydrothermically-processed for 18hours and sintered for 3hours. After homogenous beta-TCP powder mixed with aquadest in magnetic stirrer acquired, Na-alginate was add- ed during the stirring process following CaCl2 drop by drop into the mixture.Sample divided into 6-test groups ac- cording to the stirring time; P1-one hours;P2-two hours;P3-three hours;P4-four hours;P5-five hours;P6-six hours.All samples centrifuged at 2500rpm for 6minutes and freeze-dried for 12hours.PSA-test and Calcium level-test were per- formed on the sample test groups, followed by ANOVA-test and post hoc with significance level of P-value=0,05. Re- sults: Data showed average of particle-sizes P1=±336.44; P2=±325.7; P3=±340.94; P4=±452.6; P5=±556.6; P6=± 593.93.ANOVA-test result indicated a significant difference and backed up by Gomes howell test result.Significant differences were found between group first-second-third and group four-five-six also between group five and group six. Calcium level test result was P1=±10.41; P2=±9.53; P3=±9.87; P4=±5.52; P5=±5.33; P6=±5.25.ANOVA-test showed a significant difference and supported by post-hoc LSD-test.Significant differences noted between group one and other groups also between group-two-three and group-four-five-six. Conclusion: In the process of Nanoencapsu- lation of Anadara-granosa-shells, particle size gradually increased and calcium level gradually decreased along with the longer stirring time was performed.
Affiliation:
- Universitas Hang Tuah, Indonesia
- Universitas Airlangga, Indonesia
- Universitas Airlangga, Indonesia
- Universitas Hang Tuah, Indonesia
- Universitas Hang Tuah, Indonesia
- Universitas Hang Tuah, Indonesia
- Universitas Hang Tuah, Indonesia
|
|
Indexation |
Indexed by |
MyJurnal (2021) |
H-Index
|
3 |
Immediacy Index
|
0.000 |
Rank |
0 |
Indexed by |
Scopus 2020 |
Impact Factor
|
CiteScore (0.2) |
Rank |
Q4 (Medicine (all)) |
Additional Information |
SJR (0.144) |
|
|
|